KDP-KD*P
磷酸二氢钾(KDP),磷酸二氘钾(DKDP)由于其拥有优越的紫外透过,高损伤阈值,双折射系数高等特性,被广泛地应用在多种工业用途(其非线性系数偏低)。这两种晶体通常被用于做Nd:YAG激光器的二、三、四倍频器件（室温条件下）。另外，它们也具有电光系数高的特点，故也被用于制作Q开关等。
Capabilities:
|
Width x Length:
|
1x1 ~ 16x16mm
|
|
Lenght:
|
0.02 ~ 20mm
|
Specifications:
|
Angle tolerance:
|
Δθ< ± 0.5°; Δφ< ±0.5°
|
|
Dimensional Tolerance:
|
(W ± 0.1mm) x (H ± 0.1mm) x (L + 0.2mm/-0.1mm)
|
|
Flatness:
|
<λ/8 at 633nm
|
|
Surface Quality:
|
20/10 Scracth/Dig
|
|
Parallelism:
|
< 20 arc seconds
|
|
Perpendicularity:
|
< 5 arc minutes
|
|
Wavefront Distortion:
|
<λ/8 at 633nm
|
|
Clear Aperture:
|
Central 95%
|
|
Chamfer:
|
0.15x45°
|
|
Coating:
|
* Protective coating is required to prevent polished surfaces from fogging.
* Anti-reflective coating should be considered if low reflectivity is required. |
Properties:
|
KDP
|
KD*P
|
|
|
Chemical Formula
|
KH2PO4
|
KD2PO4
|
|
Transparency Range
|
200-1500nm
|
200-1600nm
|
|
Nonlinear Coefficients
|
d36=0.44pm/V
|
d36=0.40pm/V
|
|
Refractive Index (at 1064nm)
|
no=1.4938, ne=1.4599
|
No=1.4948, ne=1.4554
|
|
Electro-Optical Coefficients
|
r41=8.8pm/V
r63=10.3pm/V |
r41=8.8pm/V
r63=25pm/V |
|
Longitudinal Half-Wave Voltage:
|
Vp=7.65KV(l=546nm)
|
Vp=2.98KV(l=546nm)
|
|
Absorptance:
|
0.07/cm
|
0.006/cm
|
|
Optical Damage Threshold:
|
>5 GW/cm2
|
>3 GW/cm2
|
|
Extinction Ratio:
|
30dB
|
30dB
|
Sellmeier Equations of KDP:
no2 = 2.259276 + 0.01008956/(l2 - 0.012942625) + , 13.005522,, l, 2/(l2 - 400)
ne2 = 2.132668 + 0.008637494/(l2 - 0.012281043) + 3.2279924l2/(l2 -, 400)
Sellmeier Equations of DKDP
no2 = 1.9575544 + 0.2901391/(l2 - 0.0281399) - 0.02824391l2 +0.004977826l4
ne2 = 1.5005779 + 0.6276034/(l2 - 0.0131558) - 0.01054063l2 +0.002243821l4
Note: Other sizes, cut angle, coating are available upon request.